1、The Mechanical Properties of GWT
Thickness ( mm ) |
Density |
>Test standard |
Test item |
Performance index |
Value |
2.00 |
1.5 |
GB/T 1447-2005 |
Tensile |
Modulus of elasticity ( GPa ) |
11.74 |
Tensile strength ( MPa ) |
291.5 |
GB/T 1449-2005 |
Bend |
Modulus of elasticity ( GPa ) |
13.43 |
Flexural strength ( MPa ) |
274.85 |
GB/T 1843-2008 |
Impact strength |
Impact strength resistance ( KJ/m 2 ) |
≥ 150 |
2、 The aging-resistant property of GWT
Test method: Put several samples into different ovens, then set the temperature to 11 0 ℃ , record the result after 500 hours' aging treatment(Which is equal to five years natural environment).
Thickness (mm) |
Reference standard |
Test item
|
Performance index |
Before |
After |
2.00 |
GB/T 1447-2005 |
tensile |
Modulus of elasticity ( GPa ) |
11.74 |
12.10 |
|
>Tensile strength ( MPa ) |
291.5 |
288 |
GB/T 1449-2005 |
bend |
Modulus of elasticity ( GPa ) |
13.43 |
11.00 |
|
Flexural strength ( MPa ) |
274.85 |
>254.47 |
3、The tensile strength test after 100 hours of UV exposure.
Test condition
Test parameter |
Reference standard |
Power |
Irradiance |
Loop parameter |
Temperature |
Test period |
GB/T 16422.3-1997 |
UV340 |
0.76W/m3@340nm |
Illumination time: 8h Condensation time : 4h |
Illumination 60 ± 3 ℃ Condensation : 50 ± 3 ℃ |
100h | Test result
Reference standard |
Test index |
Before |
After |
GB/T 1447 - 2005 |
Maximum tensile stress ( Mpa) |
291.5 |
257 |
Tensile modulus ( Gpa) |
11.74 |
11.44 | |